Investigation of ASTM F75 Co-Cr-Mo alloy's abrasive wear behavior (ISAS 2018_168)
Arsalan Alamdari Ilkhchi1*, Mahmut İzciler2
1Gazi Üniversitesi, Teknoloji Fakültesi, İmalat Mühendisliği  , Ankara, Turkey
2Gazi Üniversitesi, Teknoloji Fakültesi, İmalat Mühendisliği  , Ankara, Turkey
* Corresponding author: arsalan.alamdari@gmail.com
Published Date: 2018-06-23   |   Page (s): 190-190   |    69     8

ABSTRACT In this study, abrasive wear behaviors of Co-Cr-Mo alloy (ASTM F75) which is produced by casting method, were investigated. The prepared test samples were subjected to abrasive wear tests with different emery papers on the pin on disc wear device. In the abrasive tests, 400, 600 and 800 mesh emery papers were used and abrasive wear tests were performed under loads of 5, 10 and20 N. The tests were carried out at 22 oC temperature, at a shear rate of 0.8 m / s and at a length of100 cm shear distance. EDS elemental analysis was performed to investigate the elements andchemical constituents on the surfaces of the samples and EFM surface analysis was performed toexamine the qualities and roughness of the surfaces. The obtained results showed less weight loss at the higher meshes. It was observed that better quality surfaces were found in tests which were performed in higher mesh sizes.

KEYWORDS ASTM F75 Co-Cr-Mo, Abrasive Wear, Surface Roughness, Pin on Disc
REFERENCES

SET Technology - Turkey

eISSN  : 2618-6446

E-mail : info@set-science.com
+90 533 2245325

Tokat Technology Development Zone Gaziosmanpaşa University Taşlıçiftlik Campus, 60240 TOKAT-TURKEY
©2018 SET Technology