Investigation of Mechanical Properties of The Milled Glass Fiber Powder Reinforced Polypropylene Composite (ISAS 2018_4)
Mehmet Ekici1*, Uğur Özsaraç2
1Yalova University, Yalova, Turkey
2Sakarya University, Sakarya, Turkey
* Corresponding author: mekici@yalova.edu.tr
Published Date: 2018-06-23   |   Page (s): 2-2   |    81     14

ABSTRACT In this study, the mechanical properties of milled glass fiber reinforced polypropylene matrix composite materials produced by extrusion method were investigated. The grain sizes of the milled glass fiber powders were measured with an optical microscope and were determined as 150 μm, 250 μm, 500 μm, 710 μm and 900 μm. In all experimental studies the reinforcement rate was determined to be 30%. Polypropylene matrice was added 1% maleic anhydride as initiator. The mechanically stirred solution was added as a cobalt octoate accelerator at 0.035%. Tensile and impact test specimens were prepared according to ASTM D790M-92 and ASTM D638M-91 standards to examine the mechanical properties of glass fiber reinforced polypropylene matrix composites. When the results were examined, the increase of the milled glass fiber grain size and the increase of the mechanical properties were determined. 
KEYWORDS Glass fiber powder, polypropylene composite, mechanical properties
REFERENCES

SET Technology - Turkey

eISSN  : 2618-6446

E-mail : info@set-science.com
+90 533 2245325

Tokat Technology Development Zone Gaziosmanpaşa University Taşlıçiftlik Campus, 60240 TOKAT-TURKEY
©2018 SET Technology